Permo Flow Hiper Hyper Plasticizer for Concrete

Description
Permo Flow Hyper is a hyper plasticizer ensuring a very effective fluidity in concrete production and retardation in setting in hot climate conditions. It also decreases the ratio of water significantly to acquire a high final strength. Due to this decreased water/cement ratio, the waterproof characteristic of the concrete is improved.
Usage Areas
• Allows the production of Self-Compacting Concrete (SCC).
• Floor, foundation and field concrete; curtains, girders and columns
• Reinforced concrete elements with thin and thick reinforcement
• All types of engineering buildings
• Ready-mixed concrete production and/or production at site, in summer, to be able to transport for a longer period of time.
Advantages
• Because it decreases the amount of mixing water significantly the concrete obtained is partly waterproof.
• Ensures high unit weight and resistance.
• Provides the concrete with a self-compacting characteristic.
• Protects the consistency of the concrete and allows the production of pumpable concrete which is consistent even in hot summer.
• Increases the frost resistance.
• Because it does not contain any chloride, there is no risk of damage for the reinforcement of the concrete.
• Decreases the carbonation rate of the concrete.
• Decreases concrete shrinkage significantly.
• Because it eliminates vibration, it also prevents noise pollution.
Application
At Concrete-Mixing Plants:
In the production of ready-mixed concrete, it is added to concrete mixing water found in the mixer. For best results, it is preferably better to feed water simultaneously with the additive. Concrete mixer should run at high speed for 3 minutes. Concrete prepared with mixing water should not be fed with extra water. Each 10 litres of extra water added leads to a decrease of 10 kgf/cm² in the the pressure strength of concrete.
For instance:
Quality Kontrol Tests      Unit  Result
Consistency Loss           ΔS    1
Slump 0'                      cm    23
Slump 0'                      cm    22
Spread Loss                 ΔF     4
Spread 0'                     cm    50
Spread 0'                     cm    46
Consumption
Depending on the performance expected; the amount of the product to be used should be 0,4% to 1,0% of the weight of the binder for plastic and fluid concrete. That is 400 to 1000 g for 100 kg of binder. For self-compacting concrete, the amount of the product to be used should be 1,0% to 2,0% of the weight of the binder. That is 1000 to 2000 g for 100 kg of binder. In determining the consistency, it is critical to avoid adding extra water. The concrete contains slag and silica fume as well as cement. Optimum dose depends on the quality of the binder and aggragate, the water/binder ratio and the ambient temperature.
So it is recommended to determine the optimum dose by trying different mixtures and testing them beforehand.
Packaging
IBC 1100 KG

PROPERTIES

RESULTS

STANDARD

Base

Polycarboxylate

 

Colour

Yellowish

 

Appearance

Clear, Liquid

 

Solid Content (%)

34 ± 1

EN ISO 480-8

Specific Gravity, 25/25 °C

1.00-1.10

ASTM D-7777

Viscosity 25 °C (cP)

<250

ISO 2555

pH (25 0C)

>2

ISO 4316