Em-Poxy A - Epoxy Primer

Descriptiopn
It is a double-component, epoxy-based, non-solvent, transparent undercoating material with low viscosity.
Usage Areas
It is used as an undercoat on concrete, metal, wood, asphalt, etc. before the application of polyurethane coatings and epoxy-based top coating systems.
Surface Preparation
• Pressure strength of the concrete to be treated must be 25 N/mm2 minimum and tensile strength 1,5 N/mm2 minimum.
• The humidity ratio in the concrete must be lower than 5%.
• The surface to be treated must be clean and dry and free from any other substance such as dirt, grease, old coatings and curing materials.
• Gaps and holes must be completely cleared first and then filled with Em-Poxy A which is prepared in paste form by adding sand.
• To ensure a smooth surface any swelling must be levelled.
• All dust and loose and displaced particles must be removed by using a brush and/or vacuum cleaner.
• During application relative humidity must not exceed 50% when the ambient temperature is +10°C, and 80% when the ambient temperature is +30°C.
• The temperature of the surface to be treated must be between +10°C and +30°C.
• The temperature of the surface to be treated must be 3°Chigher than the dew point.
• Ambient temperature and surface temperature must be increased by using heaters for the applications performedin cold weather conditions and Em-Poxy A containers must be kept under +20°C the previous night.
Application
First stir Component A and Component B separately, and then add Component B to Component A and stir the mixture
continuously to a homogenous consistency with a low speed mixer for 3 minutes. To minimize air drag avoid stirring too
much. The mixture should be applied to the prepared surface with a roller or trowel. It may require a second coat if it is
applied onto an absorbant surface. It is critical to apply the second coat on time. Otherwise decreased adherence may
lead to cleavage.
Consumption
Approximately 0,150-0,300 kg/m2 depending on the absorbance of the surface to be treated.
Packaging
10 kg (Component A) + 5 kg (Component B) = Net 15 kg as a set

 

COMPOSITION                        : A+B (epoxy+hardener)
MIXING RATIO                        : 10+5 KG
SOLID CONTENT                     : % 100
HARDNESS                             : >85 SHORE A
APPLICATION TEMPERATURE    : 10-35°C
SPECIFIC GRAVITY                  : at 20°C  1,05 gr/cm3 (±0,01)
POT LIFE                                : 40 min (at 20°C’de,%50 RH)
TOUCH DRY                            : 6 Hours
PEDESTARIAN TRAFFIC            : 12 Hours
FINAL CURING TIME                : 7 Days